Mechanical Property Measurement of 0.5--m CMOS Microstructures

Michael Lu, Xu Zhu, and Gary K. Fedder
MRS 1998 Spring Meeting, May, 1998.


Download
  • Adobe portable document format (pdf) (171KB)
Copyright notice: This material is presented to ensure timely dissemination of scholarly and technical work. Copyright and all rights therein are retained by authors or by other copyright holders. All persons copying this information are expected to adhere to the terms and constraints invoked by each author's copyright. These works may not be reposted without the explicit permission of the copyright holder.

Abstract
Measurements are reported on the mechanical properties of high-aspect-ratio micromechanical structures formed using a conventional 0.5-? CMOS process. Composite structures are etched out of the CMOS dielectric, aluminum, and gate-polysilicon thin films using a post-CMOS CHF3:O2 reactive-ion etch and followed by a SF6:O2 silicon etch for release. Microstructures have a height of 5 ? and beam widths and gaps down to 1.2 ?. Properties are strongly dependent on the relative metal and dielectric content of the beams. Beams with three metal conductors and polysilicon have an effective Young's modulus of 62 GPa, residual stress of -29 MPa, and an average out-of-plane radius of curvature of 1.9 mm. Maximum Young's modulus variation is 3 GPa die-to-die, and is 9 GPa between two runs. Die-to-die variation of stress and stress gradient is poor for many beam compositions, however local matching on a die is very good. Cracking is induced in a resonant fatigue structure at 620 MPa of repetitive stress after over 50 million cycles.

Notes
Associated Lab(s) / Group(s): Microelectromechanical Systems Laboratory
Number of pages: 6

Text Reference
Michael Lu, Xu Zhu, and Gary K. Fedder, "Mechanical Property Measurement of 0.5--m CMOS Microstructures," MRS 1998 Spring Meeting, May, 1998.

BibTeX Reference
@inproceedings{Lu_1998_1486,
   author = "Michael Lu and Xu Zhu and Gary K Fedder",
   title = "Mechanical Property Measurement of 0.5--m CMOS Microstructures",
   booktitle = "MRS 1998 Spring Meeting",
   month = "May",
   year = "1998",
}